Eight Good Reasons For Mechanical Plating

    Mechanical plating is an effective means of applying zinc, tin, or other ductile metals  or mixtures thereof to metal substrates.  It has a  number of advantages over conventional plating and coating processes.

1.  The most important reason for mechanical plating is the assurance of product reliability by the elimination of hydrogen-embrittlement.  Mechanical plating is the method preferred by many engineers for hardened fasteners and stressed components.

2. Elimination of lengthy preplating and post plating baking cycles. Recently, the ASTM issue standard practices 

(ASTM B 849 and B 850) recommending baking cycles before and after electroplating to prevent hydrogen 

embrittlement. For extremely hard parts, baking cycles can be quite extensive - in some cases, as long as 40 hours.*

                  *Mechanical plating is the best way to avoid the extra expense of long baking cycles. Customers                             confirm that parts have been mechanically plated - something that cannot be done to confirm baking                     cycles. Mechanical plating has a matte finish easily distinguishable from electroplating's  bright  finish.

3.  The ability to plate parts which tangle; the glass impact media used in the process tends to prevent parts from tangling. This mechanical plating process characteristically makes this technology an ideal choice for plating hardened steel springs.

4.  The ability to plate flat parts; the media prevents flat parts from masking one another.

5. Because mechanical plating consumes all the chemistry in each process cycle, there is no build up of 

contamination in the bath. This assures users of long-term product and process consistency.

6. Mechanical plating has the ability to plate sintered metal parts (powder metallurgy) without costly impregnation.

7. The ability to apply leachant sealants after the chromate conversion coating to enhance the corrosion 

protection of the process with little incremental expense. A zinc deposit of 0.0004" with a chromate and a 

leachant sealant topcoat will get over 500 hours of ASTM B 117 salt spray; at 0.001 (one mil) process will deliver over 1000 hours.

8. Attractive economics for coating thicknesses above 0.0003". This is due primarily to the fact that in mechanical plating the process for thick coatings is only slightly longer than the cycle for thin coatings (unlike electroplating, where the plating time is directly proportional to the plating thickness).The cost of additional plating thickness in mechanical plating is only slightly more than the cost of the plating metal.